Harris®
Harris® - D620F15P - Dynaflow® Phos-Copper Brazing Alloy .050 x 1/8" x 28 Stick Tube (sold by Pound)
Item: JWHD620F1
MFG: D620F15P
loading availability
Loading price
Description
Dynaflow Melts and Flows At Temperatures Very Close To Stay Silv 15, and Provides Comparable Brazed Mechanical Properties. This Makes Dynaflow An Excellent Cost Effective Alternative To The 15% Silver Alloys. This Premium, Medium Range Silver Alloy Has Been Meticulously Formulated To Even Tighter Specifications Than Our Standard Copper-To-Copper Alloys.
Dynaflow is a frequent choice for copper brazing. The phosphorus addition makes it "self-fluxing" on copper. Its wide melting range allows operators to fill loose connections and "cap", or build up, around the finished joint. When heated above its liquidus, however, it will penetrate tight connections.
Dynaflow is also a suitable choice to braze brass. In these applications operators should take care to avoid over heating the brass and use Stay Silv® white brazing flux.
Dynaflow is a popular brazing filler metal for HVAC and refrigeration connections. It’s melting range and copper joint strength makes it an excellent, lower cost, replacement for 15% silver alloys.
Dynaflow is not recommended for brazing steel or other ferrous base metals. The phosphorus content promotes formation of a low ductility intermetallic with the ferrous base metal.
Dynaflow is a frequent choice for copper brazing. The phosphorus addition makes it "self-fluxing" on copper. Its wide melting range allows operators to fill loose connections and "cap", or build up, around the finished joint. When heated above its liquidus, however, it will penetrate tight connections.
Dynaflow is also a suitable choice to braze brass. In these applications operators should take care to avoid over heating the brass and use Stay Silv® white brazing flux.
Dynaflow is a popular brazing filler metal for HVAC and refrigeration connections. It’s melting range and copper joint strength makes it an excellent, lower cost, replacement for 15% silver alloys.
Dynaflow is not recommended for brazing steel or other ferrous base metals. The phosphorus content promotes formation of a low ductility intermetallic with the ferrous base metal.
California residents: see Proposition 65 Warning
Features and Specification
| Weight | 1.000000 |
|---|---|
| Length | 19.625000 |
| Liquidus | 1465 |
| Package Weight | 5.600000 |
| Package Length | 22.250000 |
| Package Height | 1.375000 |
| Package Width | 4.250000 |
| Width | 0.125000 |
| UPC | 684032072725 |
| UOM | LB |
| Temperature Melt/Flow | Solidus 1190°F (643.33°C), Liquidus 1470°F (798.89°C) |
| Solidus | 1190 |
| Silver Content | 6 |
| Application | Premium alloy for copper or brass. Excellent strength and ductility, use as replacement for 15%. |
| AWS Specifications | Product does not have an AWS classification |
| Brand | Harris® |
| Color | Gray |
| Composition | Phos Copper Brazing Filler Metal - Silver 6%, Phosphorus 6.1%, Copper Remainder, Other (Total) 0.15% |
| Cubic Measurement | 0.000100 |
| EAN | 0684032072725 |
| Dimensional Weight | 1.000000 |
| Height | 0.050000 |
| Fluidity Rating | 3 |