Harris® - 15636S10 - Stay-Silv® 15% Phos-Copper Brazing Alloy 1/8" Square x 36" x 10 lb. Tube

Item: JWH15636S10
MFG: 15636S10
loading availability
Loading price
/ CH


Stay-Silv® 15

Stay Silv 15 is a frequent choice for copper brazing. It has a wide melting range that allows operators to fill loose connections and "cap", or build up, around the finished joint. When heated above its liquidus, however, it will penetrate tight connections.

Stay Silv 15 is also a suitable choice to braze brass. In these applications operators should take care to avoid over heating the brass, and use Stay Silv white brazing flux.

Stay Silv 15 has historically been a popular brazing filler metal for HVAC and refrigeration connections. Its low phosphorus content provides brazed assemblies with good strength and ductility. Users should also consider Harris Dynaflow® as a lower cost option.

Stay Silv 15 is not recommended for brazing steel or other ferrous base metals. The phosphorus content promotes formation of a low ductility intermetallic with the ferrous base metal. It is sometimes used to braze selected low nickel content copper-nickel base metals, (90/10), but service suitability should be first established.

California residents: see Proposition 65 Warning

Features and Specification

Weight 10.250000
Package Width 1.000000
Package Weight 53.200000
Package Length 38.500000
Package Height 2.250000
Liquidus 1480
Length 38.250000
UPC 684032015128
Width 1.875000
Temperature Melt/Flow Solidus 1190°F (643°C); Liquidus 1475°F (802°C)
Solidus 1190
Silver Content 15
Brand Harris®
Application For copper or brass. Useful for wide clearance, .002-.006". Good ductility.
AWS Specifications BCuP-5
Color Silver
Composition Brazing Filler Metal - Silver 14.5-15.5%; Phosphorus 4.8-5.2%; Copper Remainder; Other (Total) 0.15%
Cubic Measurement 0.077800
EAN 0684032015128
Dimensional Weight 1.000000
Height 1.875000
Fluidity Rating 3