Harris® - 15636S - Stay-Silv® 15% Phos-Copper Brazing Alloy 1/8" Square x 36" 25 lb. Box (Sold by the lb)

Item: JWH15636S
MFG: 15636S
loading availability
Loading price
/ LB


Stay-Silv® 15

Stay Silv 15 is a frequent choice for copper brazing. It has a wide melting range that allows operators to fill loose connections and "cap", or build up, around the finished joint. When heated above its liquidus, however, it will penetrate tight connections.

Stay Silv 15 is also a suitable choice to braze brass. In these applications operators should take care to avoid over heating the brass, and use Stay Silv white brazing flux.

Stay Silv 15 has historically been a popular brazing filler metal for HVAC and refrigeration connections. Its low phosphorus content provides brazed assemblies with good strength and ductility. Users should also consider Harris Dynaflow® as a lower cost option.

Stay Silv 15 is not recommended for brazing steel or other ferrous base metals. The phosphorus content promotes formation of a low ductility intermetallic with the ferrous base metal. It is sometimes used to braze selected low nickel content copper-nickel base metals, (90/10), but service suitability should be first established.

California residents: see Proposition 65 Warning

Features and Specification

Weight 1.000000
Length 35.750000
Liquidus 1480
Package Weight 25.500000
Package Length 37.500000
Package Height 2.250000
Package Width 2.500000
Width 0.125000
UPC 684032015081
Temperature Melt/Flow Solidus 1190°F (643.33°C), Liquidus 1475°F (801.67°C)
Solidus 1190
Silver Content 15
Application For copper or brass. Useful for wide clearance, .002-.006". Good ductility.
AWS Specifications BCuP-5
Brand Harris®
Color Silver
Composition Brazing Filler Metal - Silver 14.5-15.5%, Phosphorus 4.8-5.2%, Copper Remainder, Other (Total) 0.15%
Cubic Measurement 0.000300
EAN 0684032015081
Dimensional Weight 2.000000
Height 0.125000
Fluidity Rating 3


picture_as_pdf msds sheet

picture_as_pdf specification sheet

picture_as_pdf warranty document