Harris® - 0620F - Harris 0® Phos-Copper Brazing Alloy .050 x 1/8 x 20" 7 Stick Tube
Item: JWH21039
MFG: 0620F
loading availability
Loading price
Description
Harris 0®
This low cost alloy is suitable for most copper-to-copper or brass joints where close tolerance can be maintained.
Harris 0 is an economical alloy designed for brazing copper to copper connections. This alloy flows quickly at brazing temperature so requires close joint tolerance, less than 0.005". is a frequent choice for copper brazing.
Harris 0 is also a suitable choice for brazing brass. In this application operators should take care to avoid over heating the brass and use Harris Stay Silv® white brazing flux.
Harris 0 is not recommended for brazing steel or other ferrous base metals. The phosphorus content will form a low ductility intermetallic with the base metal.
This low cost alloy is suitable for most copper-to-copper or brass joints where close tolerance can be maintained.
Harris 0 is an economical alloy designed for brazing copper to copper connections. This alloy flows quickly at brazing temperature so requires close joint tolerance, less than 0.005". is a frequent choice for copper brazing.
Harris 0 is also a suitable choice for brazing brass. In this application operators should take care to avoid over heating the brass and use Harris Stay Silv® white brazing flux.
Harris 0 is not recommended for brazing steel or other ferrous base metals. The phosphorus content will form a low ductility intermetallic with the base metal.
California residents: see Proposition 65 Warning
Features and Specification
Weight | 1 |
---|---|
AWS Specifications | BCuP-2 |
Brand | Harris® |
Composition | Brazing Filler Metal - Phosphorus 7.1%, Copper Remainder, Other (Total) 0.15% |
Cubic Measurement | 0.0001 |
Dimensional Weight | 2 |
EAN | 0684032010840 |
Fluidity Rating | 5 |
Height | 0.05 |
Length | 19.625 |
Liquidus Temperature | 1475°F (801.67°C) |
Package Height | 2.25 |
Package Length | 21.25 |
Package Weight | 25.5 |
Package Width | 4.5 |
Prop 65 | Yes |
Silver Content | 0% |
Solidus Temperature | 1310°F (710°C) |
Temperature Melt/Flow | Solidus 1310°F (710°C), Liquidus 1475°F (801.67°C`) |
UOM | EA |
UPC | 684032010840 |
Width | 0.125 |
Country of Origin | USA |